Luminescent properties of Y2O3:Bi3+

Presented by Mrs. Rasha MOHMMED JAFER BAKEET on 9 Jul 2013 from 17:40 to 18:40
Type: Poster Presentation
Session: Poster1
Track: Track A - Division for Condensed Matter Physics and Materials

Abstract

The luminescent properties of Y2-xO3:Bix=0.002 were investigated and the fluorescence spectra show that the luminescence is stimulated by the emission from two types of centres. These two types of centres were associated with the substitution of the Bi3+ ion for the Y3+ ion in two different sites in the crystal lattice of Y2O3 (with point symmetries C2 and S6 1,2,3,4). The emission of Bi3+ in the S6 site causes blue luminescence with maxima at 360 nm and 407 nm and in the C2 site it gives green luminescence with the maximum at 495 nm. Both these emissions is related to the 3P1–1S0 transition1,3,4,5 in Bi3+. X-ray photoelectron spectroscopy (XPS) indicate that the O2-,Y3+ and Bi3+ ions occupy more than one coordination environment. This proves the two different sites in the Y2-xO3:Bix=0.002 structure. The diffuse reflectance was measured for Y2O3 and Y2O3:Bi and there was no change in the band gap when 0.2 % mol of Bi is doped in the Y2O3 host. References (1)L.G. Jacobsohn, M.W. Blair, S.C. Tornga, L.O. Brown, B.L. Bennett, R.E. Muenchausen, Applied physics. 2008, 104,124303. (2)F. Real, B. Ordejon, V. Vallet, J. Flament, J. Schamps, Chemical physics. 2009, 131,194501. (3)O. M. Bordun. Applied spectroscopy. 2002, 69,1. (4)G. Ju, Y. Hu, L. Chen, X. Wang, Z. Mu, H. Wu, F. Kang. Electrochemical society. 2011, 158,294. (5)X. Y. Huang, X. H. Ji, Q. Y. Zhang. The American ceramic society. 2011, 94, 833.

Award

Yes

Level

PhD

Supervisor

Coetsee E coetseee@ufs.ac.za University of the Free State

Paper

Yes

Primary authors

More

Co-authors

More