Combustion synthesis of Dy3+–doped YVO4 phosphor
Presented by Ms. Emily FOKA on 8 Jul 2014 from 17:10 to 19:00
Type: Poster Presentation
Track: Track A - Division for Physics of Condensed Matter and Materials
Board #: A.337
Yttrium orthovanadate (YVO4) belongs to the space group 19D4h  and is an important optical material that has been given considerable attention due to its outstanding characteristics, such as excellent thermal, mechanical and optical properties. There are two basic approaches to generate white light from light emitting diodes (LEDs). One is by mixing light of different colours emitted by several chips called multichip LEDs and the other is to convert the light emitted from a blue or ultraviolet (UV) LED to a longer wavelength light using phosphors, which are called phosphor-converted (pc) – LEDs. In order to produce a phosphor that will produce white light for the LED applications Dy3+ –doped YVO4 phosphors were produced by a combustion method at 600oC. The structure and optical properties of the powders were investigated using X-ray diffraction (XRD), scanning electron microscopy , Fourier transform infrared spectroscopy and photoluminescence (PL). The XRD patterns showed the tetragonal phase which agreed very well with the standard JCPD file (17-0341). In the PL, the emission spectra exhibited a weak band at 663 nm for 4F9/2-6H11/2 and a peak at 283 nm for 4F9/2-6H13/2 and the 257 nm peak with a higher intensity for the 4F9/2-6H15/2 transition. The emission colour of the luminescence is close to white because of the yellow (4F9/2 → 6H13/2) and blue (4F9/2 → 6H15/2) emissions of Dy3+ and has the potential to be used as a phosphor for pc-LEDs.
Dejene FB, email@example.com