Characterization of the Phase Transition of h-BN - c-BN Nanoparticles by Ion Implantation

Presented by Ms. Emily ARADI on 15 Jul 2011 from 12:15 to 12:30
Type: Oral Presentation
Session: Applied
Track: Track F - Applied and Industrial Physics

Content

<p>The synthesis of the c-BN (cubic boron nitride) has developed great interest due to its excellent physico-electrochemical properties. These include; high hardness values (73 GPa) second after diamond, wide band gap (6.4 eV), optical transparency in a wide region of the electromagnetic spectrum, high temperature stability (1200 oC) and chemical inertness. These properties enable c-BN to be very useful for various industrial and electrical applications such as in cutting and grinding, fabrication of high temperature high frequency devices among many others. In this work, ion irradiation effect of the soft graphitic boron nitride (h-BN) is investigated from characterization with Raman Spectroscopy before and after implantation. This was to investigate a possible phase transformation of h-BN to c-BN. Boron, lithium and helium ions were implanted into the hot pressed h-BN samples at 150keV, and with fluences ranging from 1x1014 ions/cm2 to 1x1016 ions/cm2. Raman Spectroscopy showed that implantation of all the three ions led to an h-BN to a possible c-BN phase transition, evident from the longitudinal optical (LO) Raman phonon features occurring at 1303cm-1 in the implanted samples’ spectra. The nature of the phonon peaks and their downshifting is explained using the spatial phonon correlation model. The extent of these peaks was found to depend on the mass of the incident ion and the fluence, where high ion mass required low fluence compared with the low ion masses.

Level (Hons, MSc, PhD, other)?

PhD

Consider for a student award (Yes / No)?

Yes

Short Paper

Yes

Place

Location:
Room: Acro3


Primary authors

More

Co-authors

More